On the Use of the Notch Master Curve for Apparent Fracture Toughness Predictions of Notched Ferritic Steels Operating Within the Ductile-to-Brittle Transition Zone

This paper presents the Notch-Master Curve as a model for the prediction of the apparent fracture toughness of ferritic steels in notched conditions and operating at temperatures corresponding to their ductile-to-brittle transition zone. The Notch-Master Curve combines the Master Curve of the material in cracked conditions and the notch corrections provided by the Theory of Critical Distances. In order to validate the model, the fracture resistance results obtained in fracture tests performed on notched CT and SENB specimens are presented. The results gathered here cover four ferritic steels (S275JR, S355J2, S460M and S690Q), three different notch radii (0.25 mm, 0.50 mm and 2.0 mm) and three different temperatures within the corresponding ductileto-brittle transition zone. The results demonstrate that the Notch Master Curve provides good predictions of the fracture resistance in notched conditions for the four materials analyzed.